Estetic H
heat-curing acrylic resin for crowns and bridges

Single colors available in packages containing 100 g powder (neck, dentin, enamel set) and 50 ml solvent
G1; G2; G3; A1; A2; N2; N3; B3; R1; R3; R5;
A1V; A2V; A3V; A3,5V; A4V; B2V; B3V; B4V; C1V; C2V; C3V; C4V; D2V; D3V; D4V

Available in packages:

• 60 g DENTIN powder R1; G1; G2; A1; N3,   40 g DENTIN powder B3; R5
  60 g NECK powder G1,   60 g ENAMEL powder
  Total 500 g powder, 250 ml Estetic H solvent

• 60 g DENTIN powder A1V; A2V; A3V; A4V;B2V,   40 g DENTIN powder C2V; D3V
  60 g NECK powder A3V,   60 g NECK powder
  Total 500 g powder, 250 ml Estetic H solvent

Estetic H

• heat-curing polymer,
• is characterized by a colour stability,
• the hardness of the crowns made of ESTETIC H imitate the hardness of natural teeth,
• is produced in accordance with WIEDENT and V shade guides,
• complies with the requirements of international standard PN-EN ISO 10477:2002.

Mixing proportions:

Recommended powder/solvent mixing proportions - 2:1 w/w

Direction for use and polymerising:

Pour appropriate amounts of the solvent into two vessels and gradually add to one the powder marked DENTIN of appropriate color, and to the other the powder marked COLLET. Stir for several seconds avoiding formation of air bubbles. Cover the vessels tightly and keep under cover for ca. 15 min (depending on the temperature of the environment). Higher temperatures accelerate initial swelling. Check plasticity with a spatula. If ductile threads adhere to the spatula when it is removed from the mass, the material is ready for molding. Mold the shell crown or facings modeled in wax according to the commonly used method. After opening the mold, melt off the wax and applying an isolating layer onto plaster surface, cool the mold to room temperature. Apply a thin layer of Estetic Ekri - priming opaquer onto metal surfaces to be faced and leave to dry completely. Place plastic COLLET material in the collet portion of the denture, forming the remaining part of the DENTIN material. Form the junction site with spatula and wet with the monomer to obscure the borderline between the layers. Press through wet cellophane layer with gradually increased pressure, and leave for min. 1 minut. After insert in the polymerizing tin in a polymerizing frame and immerse the frame in boiling water and maintain the boiling temperature for 20 min. Turn off the heat source, cool the mold to room temperature and open. Abrade the faced surface to prepare it for ENAMEL layer application. File off a 1-1.5mm layer off the incisal edges and cusps, with gradual reduction of filed-off thickness towards the neck. Mix the ENAMEL powder with the solvent in the same way as DENTIN and COLLET material. Apply the solvent onto the filed facing surface, then apply the plastic material, form and mold under pressure. Polymerize as described above. Process and polish with generally used methods.

The manufacturer recommends the following guidelines to be included in instructions for the patients:

• crowns and bridges made up of ESTETIC H should be washed with a tooth-brush and toothpaste;
• damaged crowns and bridges should be repaired only by a dental technician or a dentist,
• the adjustment of crowns and bridges should be regularly checked by a dentist.